Spray Coated Cellulose Nanofiber (CNF) Film as an Eco-Friendly Substrate for Flexible and Printed Electronics
Online Journal of Engineering Sciences
| Vol 1, Issue 1
Table 1. Summary of Surface Roughness of CNF film via various method
| Films Preparation method | Technique used | Surface | RMS Roughness | |
| Spray Coating | Atomic Force Microscopy | Rough | 414.0 nm (10µm x10µm) | 51.4 nm (2µm x 2µm) |
| Smooth | 81.1 nm (10µm x10µm) | 16.7 nm (2µm x 2µm) | ||
| Optical Profiler 50x Image | Rough Smooth | 2086.69 nm 389 nm | ||
| Vacuum Filtration | Atomic Force Microscopy | Free Side | 417.7 nm (10µm x10µm) | 102.3 nm (2µm x 2µm) |
| Filter side | 330.8 (10µm x10µm) | 70.7 nm (2µm x 2µm) | ||
| Optical Profiler 50x Image | Free Side Filter Side | 2673 nm 3751 nm | ||